Μαχαίρια πάστας
Δείκτης: 0RS006-1L
GLASS LIGHT FILLER: 0RS006-1L
Super light filler with fiberglass. It features a creamy consistency that allows for easy modeling in layers of 2 - 4 mm and sanding with high grit abrasives. The ability to use higher grit abrasives (coarse sanding P120 - P150) and the adjusted hardness of the filler to paint coatings eliminates the formation of transitions between the filler and the repaired surface. Thanks to this, the filler can also be used directly under the filling primer. The filler is especially intended for repairing large, very damaged surfaces.
For filling irregularities on steel, aluminum, galvanized, and polyester-glass surfaces. Intended for manual and machine processing with dry abrasives, it does not clog sandpaper during sanding. It can be easily modeled even on surfaces with complex shapes, even when applying thicker layers. It has very good adhesion to the substrate and is used, among other things, to reinforce surfaces weakened after bodywork repair, increasing the mechanical strength of the repaired element.
Usage:
The repaired substrate must be clean, dry, degreased, and matted. Thoroughly mix the filler mass with the hardener in an amount of 2-3% by weight, then apply to the substrate for about 5 minutes at 20 oC - higher temperature shortens the product's life and accelerates the curing process.
WARNING: Overdosing the hardener may cause discoloration of the topcoat. It is not recommended to use the product at temperatures below 15 oC.
Περιγραφή
GLASS LIGHT FILLER: 0RS006-1L
Super light filler with fiberglass. It features a creamy consistency that allows for easy modeling in layers of 2 - 4 mm and sanding with high grit abrasives. The ability to use higher grit abrasives (coarse sanding P120 - P150) and the adjusted hardness of the filler to paint coatings eliminates the formation of transitions between the filler and the repaired surface. Thanks to this, the filler can also be used directly under the filling primer. The filler is especially intended for repairing large, very damaged surfaces.
For filling irregularities on steel, aluminum, galvanized, and polyester-glass surfaces. Intended for manual and machine processing with dry abrasives, it does not clog sandpaper during sanding. It can be easily modeled even on surfaces with complex shapes, even when applying thicker layers. It has very good adhesion to the substrate and is used, among other things, to reinforce surfaces weakened after bodywork repair, increasing the mechanical strength of the repaired element.
Usage:
The repaired substrate must be clean, dry, degreased, and matted. Thoroughly mix the filler mass with the hardener in an amount of 2-3% by weight, then apply to the substrate for about 5 minutes at 20 oC - higher temperature shortens the product's life and accelerates the curing process.
WARNING: Overdosing the hardener may cause discoloration of the topcoat. It is not recommended to use the product at temperatures below 15 oC.